cross-linking copolymer

基本解释

Results also indicate the T_g of one copolymer increases from(31.21) ℃ to(53.12) ℃, and pencil hardness is more than 4H by using cross-linking catalyst.
催化交联剂可使共聚物的玻璃化温度从31.21℃提高到53.12℃，膜的铅笔硬度达到4H以上。
Foamed cross-linking ethylene-vinyl acetate copolymer(EVA) material with high elasticity was a kind of new foamed material which had wide future of using.
高弹性乙烯-乙酸乙烯共聚物（EVA）交联发泡材料是一种具有广阔应用前景的新型发泡材料。
The influence of the cross-linking agent amount, initiator and its amount, reaction temperature and monomer ratio time on the water absorbency of the graft copolymer were investigated.
研究了共聚物的反应温度、单体的配比、引发剂种类与用量、交联剂用量对吸水率的影响。

交联共聚物
Based on dynamic viscoelasticity experiment, it shows that the crosslinking copolymer form more hydrophobic associative structure, which results in the viscoelasticity is obvious.
动态粘弹性实验研究发现,交联共聚物形成了更多的疏水缔合结构,体系的弹性特征明显增强。